- Primerless to glass
- 3 Hour Minimum Drive Away Time (MDAT); tested according to FMVSS 212
- Can be used for non-conductive applications
- Short cut-off string
Sikaflex® P2G PLUS has been specifically designed for the Automotive Glass Replacement business. It is ideal for mobile and in-shop installations. This product is to be used by professional, experienced users only. For other applications, tests with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.
SPECIFICATIONS
Chemical base
1 Component Polyurethane
Color (CQP001-1)
Black
Cure Mechanism
Moisture-Curing
Non-sag properties
Excellent
Application temperature
Product 10 – 35 °C (50 – 95 °F), Ambient 4 – 43 °C (40 – 110 °F)
Skin time (CQP019-1)
30 minutes
Open time (CQP526-1)
15 minutes
Tensile strength (CQP036-1 / ISO 527)
5 MPa (750 psi)
Elongation at break (CQP036-1 / ISO 527)
400 %
Tensile lap-shear strength (CQP046-1 / ISO 4587):
3 MPa (400 psi)
Service temperature (CQP509-1 / CQP513-1)
-40 – 93 °C (-40 – 200 °F)
CQP = Corporate Quality Procedure
A) 23 °C (73 °F) / 50 % r.h. B) Stored below 25 °C (77 °F)
APPLICATION LIMITS
Avoid contact with alcohol and alcohol containing solvents during cure.
Do not apply over silicones or in the presence of curing silicones.
Glass parts must always be installed within the open time. The open time is significantly shorter in hot and humid climates. Never install any glass part after the product has built a skin.
NOTE
Please be aware that SIKA products do not come with a 1:1 ratio of nozzles. Each case of 10 cartridges includes ONLY 7 nozzles. This is consistent with industry standards, where the average usage is approximately 1.5 cartridges per application.
If additional nozzles are required, reference under catalog number PP1N0Z (pack quantity: 6) to purchase separately.
Product images shown are of the actual product or a close representation. Colors can vary depending on your computer's video card and on how your monitor's color is adjusted.